| Mudell | DK417 | DK417-3 | DK417-5 | DK417-8 | | Fażi tal-kristall | Fażi monoklinika | 3y fażi tetragonali | 5y fażi tetragonali | Fażi 8ykubika | | ZRO2% (+ HFO2) | 99.9 | 94.7 | 91.5 | 86.5 | | Y2O3 （WT%） | - | 5.3 ± 0.3 | 8.5 ± 0.3 | 13.5 ± 0.3 | | Al2O3% ≤ | 0.005 | 0.01 | 0.01 | 0.01 | | Sio2% ≤ | 0.005 | 0.01 | 0.01 | 0.01 | | Fe2O3% ≤ | 0.003 | 0.01 | 0.01 | 0.01 | | Cao% ≤ | 0.003 | 0.005 | 0.005 | 0.005 | | Mgo% ≤ | 0.003 | 0.005 | 0.005 | 0.005 | | Tio2% ≤ | 0.001 | 0.002 | 0.002 | 0.002 | | Na2o% ≤ | 0.001 | 0.005 | 0.01 | 0.01 | | Cl-% ≤ | 0.1 | 0.1 | 0.1 | 0.1 | | Ħruq% ≤ | 0.8 | 0.8 | 0.9 | 0.85 | | Id-daqs medju tal-partikula | 20nm | 20nm | 20nm | 20nm | Firxa ta 'Applikazzjoni: 1. Addittivi tal-batterija: L-istabbilizzazzjoni tan-nano-zirconia bħala elettrolit ideali intuża ħafna fiċ-ċelloli tal-fjuwil tal-ossidu solidu. 2. Ċeramika funzjonali, ċeramika strutturali: ċeramika elettronika, bijoramika, ċeramika tas-sensuri, materjali manjetiċi, eċċ.; Nano-Zirconia ttejjeb l-ebusija, il-finitura tal-wiċċ u d-densità taċ-ċeramika ta 'partijiet strutturali taċ-ċeramika. 3. Kisi tal-isprej, element pjeżoelettriku, resister sensittiv għall-ossiġnu, kapaċitatur ta 'kapaċità kbira. 4. Ġebel artifiċjali, materjali li joborxu, materjali tal-illustrar. Materjali tal-Kisi Funzjonali: Miżjud mal-kisi biex ikollu effett kontra l-korrużjoni, kontra l-batterja, itejjeb ir-reżistenza għall-ilbies. 5. Nano-Zirconia jintuża għal materjali refrattarji: kuxxinett ta 'appoġġ elettroniku taċ-ċeramika, ħġieġ imdewweb, refrattarju tal-metall metallurġiku. |
Dak li nistgħu nipprovdu ： 